High Quality Stearic Acid Amide Emulsion

Stearic Acid Amide Emulsion:
Stearic acidamideamide, a white emulsion that is not toxic, polluting, hazardous, or environmentally harmful, is a non-toxic product. The product can be easily dispersed in water, has low viscosity and is highly dispersible.
Stearamide may also be known as stearamide. Its chemical formula for stearamide is C17H35CONH2. Stearic acidamideamide is insoluble when mixed with water. It can be slightly soluble at room temperature in organic solvents. It is able to improve dispersion effects and the affinity of dyes.
Excellent adhesion and lubricity. No moisture absorption. You can mix it with paraffin wax. Ammonium salt is created by the reaction between stearic and ammonia. It then gets dehydrated to get the final product. This salt has excellent lubricity as well as mold release capabilities. Use it as a pigment ink mixed agent, surface-active and fiber oil agent.
The use of stearamide in thermal paper coatings can serve as both a sensor and slip agent, and as an anti-blocking and slip agent for polyolefin films. The base of stearates is fatty saturated linear monocarboxylic oils derived from natural vegetable oil. Send an inquiry for the most current price to purchase bulk Stearic Acid Amide Emulsion.

Technical Information of Stearic Acid Amide Emulsion:

How does Stearic Acid Amide Emulsion get made?
Insoluble in water, stearic Acid amide must be prepared using emulsifiers. The water-based stearic acids amide already exists, but it still shows poor dispersion even after adding an emulsifier. Additionally, precipitation can occur from long-term storage. Additionally, high-speed stirring is required and the grinding must be done under heat. The production costs are high.

First, add the water-based water-basedstearic Acid amide to the water. Next stir for 60 minutes at 2500r/min. Then add defoamer (stirring frequency is 2500r/min) and continue stirring for another 40 min. To obtain the aqueous solution of stearic Acid amide amide. This prepared water-based, stearic-acid amide-amide emulsion contains 41.7% solids. It has a viscosity level of 146 mPa*S. After 30 minutes of centrifugation at 20000r/min, the defoamer and preservative were added to the mixture. Stearic-acid amide emulsion was kept at 20-35 degC for three months with no flocculation or delamination.

Applications for Stearic Acid Amide Emulsion:
Stearamide can be used to lubricate and release molds for polyvinylchloride, polystyrene, and other plastics.
As an antiblocking agent to polyolefin film films, stearamide should be combined with oleamide-erucamide.
Stearamide, unlike the common inorganic anti-blocking agents (silica), does not affect the transparency. Stearamide is used to release synthetic rubber, natural rubber and as a lubricant for rubber compound processing. This gives it a high Gloss.
The sensitizer of thermal paper is made from stearic Acid amide Ultrafine Aqueous Dispersion.
The ultra-fine, water-based, stearic Acid amide dispersion serves as textile waterproofing, fabric softener and antistatic agent. It also acts as a wetting agent.