Aluminum silicide also goes by the name aluminum disilicide. Its chemical formula is AlSi2. Powdered aluminum silicide is also known as AlSi2 and can be used in powder metallurgy, brazing solder, and other applications.
Purity: 99%
Particle size 5-10um
Aluminum Silicide AlSi2 Pulver:
Alloys of aluminum and silicon
Aluminium-silicon alloy is an alloy made by forging or casting aluminum with silicon as its major components. The average silicon content is 11 percent. A small amount of iron and copper are also added to improve the strength. The density of the material is approximately 2.62.7. It is around 2.62.7 g/cm3. The thermal conductivity of the material is 101126W/(m*), Young’s modulus 71.0GPa. Impact value 78.5J. Fatigue limit +-45MPa.
Because of its light weight, high thermal conductivity, certain strength, hardness and corrosion resistance
AI-Si Alloys
These are commonly used in automotive manufacturing and machine building to create parts that can be used under sliding friction conditions.
The
aluminum-silicon alloy
It forms a binary phase in 11.7% silicon, with a melting point at 577degC. Both phases can be described as silicon solid solutions of aluminum and silicon solid solutions of aluminum at room temperature. Intermetallic compounds do not exist. You can add sodium in very small quantities to increase the eutectic strength and harden the dispersion. Although iron is not a very good choice, it can significantly reduce toughness. However, manganese may be used to mitigate this.
Al-Si alloy
This is an industrial metal that's very valuable.
Aluminium silicide
This metal is extensively used in the construction of automobiles, aircraft, transport, and construction industries. This is used for making low- or medium-strength castings of complex shapes like brackets and motor housings. Brazing solder is also made from racks. It is a typical eutectic alloy with a simplified phase diagram. No intermediate compounds are made. This alloy offers high casting performance, low specific strength, and low prices. It is an element in the third group of elements, with silicon being a semiconductor element. The difference between them is small.
To receive the latest information, send us an inquiry
aluminum disilicide price
You can buy here
Aluminum silicicide AlSi2 powder
In bulk.
The Product Performance of AlSi2 Aluminum Silicide Powder
Aluminum silicide AlSi2 (powder) is an alloy from silicon and aluminium. The aluminum silicide, which is often in the form or powder, is used as a material raw material in powder metallurgy. Aluminium silicide is formed at high temperatures into a liquid and then pressed into different products.
Technical Parameters of AlSi2 Powder Aluminum Silicide:
Name of Product
|
MF
|
Purity
|
Particle Size
|
Melting Point
|
Density
|
The color of the sky
|
Silicide of aluminum
|
AlSi2
|
99%
|
5-10um
|
1400
|
2.7g/cm3
|
gray-black
|
Chemical composition of AlSi2 Powder Aluminum Silicide:
AlSi2
|
Al
|
Si
|
Fe
|
Ca
|
S
|
P
|
C
|
99%
|
70%
|
Balance
|
0.2%
|
0.1%
|
0.02%
|
0.05%
|
0.02%
|
It is simple.
Aluminum silicicide AlSi2 Powder
produced?
An electrothermal process for making aluminum-silicon alloy is at around 2000 degC. Alumina and silicon oxide, which are liquids during the metallurgical processes, are reduced by a carbonaceous agent. The maximum temperature the submerged arcane can achieve is usually about 1350 to about 2200 degC.
Applicaciones
Aluminum Silicide AlSi2 (Powder)
The ductility of an aluminum-silicon alloy is best when it has a low silicon content (such 0.7). It is also more malleable and can often be used as deformed alloy. But, when it has a higher silicon content (such 7%), it fills the melt better and is frequently used in the production of Cast alloy.
When the aluminum-silicon alloys have a silicon content greater than 12.6% (silicon particle content as high as 14.5% or 25%), adding some Ni, Cu, Mg, and other elements to the alloy can increase Its complete mechanical properties.
These can be replaced by cast iron cylinders for a significant weight reduction. You can electrochemically treat the aluminum-silicon cylinder to remove the surface aluminum, retain primary silicon dots embedded within the substrate of the cylinder and improve its wear and scratch resistance.
Due to its low weight and corrosion resistance, an alloy with between 11%-13% silicon content is one of the top piston materials.
1). Powder metallurgy materials made of aluminum silicide, AlSi2 (powder) are used. The silica at high temperatures is able to form into a molten state, which can then be pressed into many different products.
2). AlSi2 aluminum silica powder is used for the production of weak castings in complex shapes, like bracket, cover and motor shell.
3). As brazing solder, AlSi2 silicide AlSi2 is used.
Shipping and Packing of Aluminum Silicide AlSi2 Pulver:
There are many options for packing, which depend on the amount of aluminum silica AlSi2 powder.
Powder packaging of aluminum silicicide AlSi2
You can vacuum pack 1kg/bag or 25kg/barrel.
Aluminium silicide AlSi2 Powder shipping
Could be sent by sea, air, or express once payment receipt is received.
Eduloc advanced materials Nano Technology Co. Ltd. (Eduloc), is an established global supplier of chemicals and manufacturers with more than 12 years experience. They offer super high quality chemical products, Nanomaterials, as well as graphite powder, boride powder and sulfide powder.
High-quality products are what you want
Al
Si2
Pulver
Please feel free and contact us to make an enquiry. (
brad@ihpa.net
)