High Purity Zinc Selenide ZnSe Powder CAS 1315-09-9, 99.9%

Zinc selenide, with the chemical formula ZnSe has a molecularweight of 144.33. This solid, light-colored compound is insoluble when dissolved in water. You can make it by reacting with zinc chloride or zinc sulfate. With hydrogen selenide. Useful in laser medicine, astronomy, night vision, and other fields. A yellow transparent, polycrystalline zinc selenide substance has a crystal size of 70 mm. It also has a light transmission range between 0.5-15m. Chemical vapor deposit (CVD), is a method that does not absorb impurities and has a very low scattering loss. This material is the best choice to make optical devices using high-power CO2 lasers because of its low absorption at 10.6mm wavelength. Additionally, this material is used frequently in other optical systems throughout its light transmission spectrum.

Specification ZnSe Zinc Selenide Powder :
Zinc Selenide, MF	ZnSe
Zinc SelenideColor	light yellow
Zinc Selenide Weight	144
Zinc SelenideMelting point	1100
Zinc SelenideCAS	1315-09-9
Zinc SelenideEINECS Nr.	215-259-7
Zinc Selenide density	5.42 g/cm3

It is simple. Zinc Selenide ZnSe Powder produced?
Zinc selenide may be made by heating ZnSO4 solution and H2Se, or ZnO and ZnS together and heating them to 800. This is used to catalyze the organic synthesis from isopropanol of acetone. A phosphatphor is an organic compound which contains Cd but has a low amount of Zn.
1. A dilute solution of zinc sulfurate, buffered by ammoniumacetate, is added into the saturated H2Se solution. H2Se gas is then diluted or added to this solution. Heat the precipitated vessel in a steambath. After that, add H2Se gas diluted with N2 or H2 to the solution. Zinc salt solutions that are too concentrated or too quickly introduced will cause white precipitates. These precipitates will not change into yellow ZnSe and will need to be removed by centrifugation. After the separation, it was first washed in boiled ammonia then dried with methanol. After the ZnSe precipitates had been cleaned, they were dried first in a vacuum dryer with CaCl2. Next, it was dried at 120° C in a dryer with P2O5.
Zinc selenide reacts very strongly to moisture. The dried product should be placed inside a glass tube and heated to 600 °C in H2 or Se atmosphere for 2 - 4 hours to get rid of the oxidized products.
2. The mixture of four grams zinc oxide, two-thirds of a cup zinc sulfide, and six grams selenium were placed inside a quartz crucible with the lid. After heating at 800 for 15 min, the ZnSe product was obtained.

Applicaciones Zinc Selenide ZnSe Powder
ZnSe is produced in melt with excess inert gases pressure (usually Ar). ZnSe is ideal for use in 10.6 mm wavelength CO2 laser optics as it does not absorb or include any inclusions. ZnSe therefore is an infrared important material. It can transmit wavelengths of 0.45 21.5mm. Green had a refractive Index of 550nm, while the LWIR refractive Index was 10.6mm. ZnSe can also be used for:
1. ZnSe is a good choice for both fluorescent materials and semiconductor dopants.
2. ZnSe has a wide range of uses in medicine, laser, and infrared.
3. Znse is used in the manufacture of infrared transmissible materials and optical instruments
4. ZnSe is used for the formation of an IIVI LED and diode-laser. It emits blue light.
Infrared laser gain medium for Cr Doped ZnSe, (ZnSe : Cr), has an emission wavelength approximately 2.4 mm.
5. A scintillator with a wavelength of 640nm called Activated ZnSe is suitable to match the photodiode. It can be used in X-ray and gamma ray detectors. ZnSe scintillator has a distinct design.